wendy@yxgmcj.com
+86-0510-87491823
- Advanced Ceramics
- Engineering Ceramics
- Ceramic Insulator
Zirconia Tube Ceramic Parts Zirconia Pipe
Payment Type:T/T,Paypal,Others
Incoterm:FOB,CIF,EXW,DDP,FCA
Transportation:Ocean,Land,Air,Express
Port:Shanghai,Shenzhen,Ningbo
option:Product DescriptionProduct AttributesBrand: YXGM
Place Of Origin: China
Species: Ceramic Parts
Application: Industrial Ceramic
Material: Zirconia Ceramic
Processing Service: Cutting, Punching, Moulding
Color: White
Density: 3.7-6.05g/cm3
Application: Industrial Machinery
Certification: ISO9001:2015,ROHS
Supply Ability & Additional InformationPackaging: Pallet
Productivity: 200000pcs/month
Transportation: Ocean,Land,Air,Express
Place of Origin: CHN
Supply Ability: 200000pcs/month
Certificate: ISO9001:2015,ROHS
HS Code: 8547100000
Port: Shanghai,Shenzhen,Ningbo
Payment Type: T/T,Paypal,Others
Incoterm: FOB,CIF,EXW,DDP,FCA
Packaging & DeliverySelling Units:Piece/PiecesPackage Type:PalletPicture Example:
Ceramic lamp holderZirconia Tube Ceramic Parts Zirconia Pipe
Zirconia tube ceramic parts, also known as zirconia pipe, are precision-engineered components made from ZrO2 Ceramics, a type of Advanced Ceramics known for their exceptional strength, hardness, and thermal properties. These ceramic parts are commonly used as ceramic insulators in various industrial applications where high temperature resistance and electrical insulation are required. Zirconia tube ceramic parts offer superior performance and durability compared to traditional insulating materials, making them an ideal choice for demanding environments.
Technical Parameters:
Item Unit Al2O3 95％－97％ Al2O3 99％ Desity g/cm3 3.7 3.85 Flexural Strength Mpa 300 340 Compressive Strength Mpa 3400 3600 Modulus of Elaslicity Gpa 350 380 Impact Resistance Mpa m1/2 4.0 5 Weibull Moudulus m 10.0 10 Vickers Hardness HV0.5 1200.0 1300 Thermal Expansion Coefficent 10-6K-1 5.0-8.3 5.4-8.3 Thermal Conductivity W/mK 24 27 Thermal Shork Resistance △T℃ 250 270 Maximum Use Temperature ℃ 1600 1650 Volume Resistivity at 20℃ Ω ≥1014 ≥1014 Dielectric Constant KV/mm 20 25 Open Porosity % 0 0 Dielectric Constant ξr 10 10 Dielectric Loss Angle Tanσ 0.001 0.001
Item Unit ZrO2 ZTA Desity g/cm3 6.05 4.1 Flexural Strength Mpa 1300 480 Compressive Strength Mpa 3000 3300 Modulus of Elaslicity Gpa 205 320 Impact Resistance Mpa m1/2 12 7 Weibull Moudulus m 25 15 Vickers Hardness HV0.5 1150 1600 Thermal Expansion Coefficent 10-6K-1 10 9 Thermal Conductivity W/mK 2 20 Thermal Shork Resistance △T℃ 280 260 Max Useage Temperature ℃ 1000 1600 Volume Resistivity at 20℃ Ω ≥1010 ≥1012 Open Porosity % 0 0