99% Alumina Ceramic Stick with Pink Color
Payment Type:T/T,Paypal,Others
Incoterm:FCA,DDP,CIF,FOB,EXW
Transportation:Ocean,Land,Air,Express
Port:Shanghai,Shenzhen,Ningbo
-
$5500-49999Piece/Pieces
$4.5≥50000Piece/Pieces
option:Product DescriptionProduct AttributesBrand: YXGM
Place Of Origin: China
Species: Ceramic Parts
Application: Industrial Ceramic
Material: Alumina Ceramic
Processing Service: Cutting, Punching, Moulding
Material: 95-99%Al2O3,ZTA,ZrO2 ceramics
Color: White
Density: 3.7-6.05g/cm3
Application: Industrial Machinery
Certification: ISO9001:2015,ROHS
Supply Ability & Additional InformationPackaging: Pallet
Productivity: 200000pcs/month
Transportation: Ocean,Land,Air,Express
Place of Origin: CHN
Supply Ability: 200000pcs/month
Certificate: ISO9001:2015,ROHS
HS Code: 8547100000
Port: Shanghai,Shenzhen,Ningbo
Payment Type: T/T,Paypal,Others
Incoterm: FCA,DDP,CIF,FOB,EXW
Packaging & DeliverySelling Units:Piece/PiecesPackage Type:PalletPicture Example:
Textile ceramics goodHigh Precision Polishing Zirconia Zro2 Ceramic Rod
High precision polishing Zirconia ZrO2 Ceramic Rod is a type of rod made from ZrO2 Ceramics, a type of ceramic that is known for its strength and durability. These rods are often used in applications that require high levels of precision and accuracy, such as in the manufacturing of precision instruments and equipment.
Zirconia ZrO2 ceramic rods are made using a process called high precision polishing. This process involves using a fine abrasive material to remove any imperfections on the surface of the rod, resulting in a smooth and polished finish. This not only improves the appearance of the rod, but also enhances its performance and longevity.
These Advanced Ceramics are highly resistant to wear and tear, making them ideal for use in high-stress environments. They are also resistant to heat and corrosion, allowing them to withstand extreme conditions without losing their shape or structural integrity.
Technical Parameters:
Item Unit Al2O3 95％－97％ Al2O3 99％ Desity g/cm3 3.7 3.85 Flexural Strength Mpa 300 340 Compressive Strength Mpa 3400 3600 Modulus of Elaslicity Gpa 350 380 Impact Resistance Mpa m1/2 4.0 5 Weibull Moudulus m 10.0 10 Vickers Hardness HV0.5 1200.0 1300 Thermal Expansion Coefficent 10-6K-1 5.0-8.3 5.4-8.3 Thermal Conductivity W/mK 24 27 Thermal Shork Resistance △T℃ 250 270 Maximum Use Temperature ℃ 1600 1650 Volume Resistivity at 20℃ Ω ≥1014 ≥1014 Dielectric Constant KV/mm 20 25 Open Porosity % 0 0 Dielectric Constant ξr 10 10 Dielectric Loss Angle Tanσ 0.001 0.001
Item Unit ZrO2 ZTA Desity g/cm3 6.05 4.1 Flexural Strength Mpa 1300 480 Compressive Strength Mpa 3000 3300 Modulus of Elaslicity Gpa 205 320 Impact Resistance Mpa m1/2 12 7 Weibull Moudulus m 25 15 Vickers Hardness HV0.5 1150 1600 Thermal Expansion Coefficent 10-6K-1 10 9 Thermal Conductivity W/mK 2 20 Thermal Shork Resistance △T℃ 280 260 Max Useage Temperature ℃ 1000 1600 Volume Resistivity at 20℃ Ω ≥1010 ≥1012 Open Porosity % 0 0