Species: Ceramic Parts
Application: Industrial Ceramic
Material: Alumina Ceramic
Processing Service: Cutting, Punching, Moulding
Material: 95-99%Al2O3,ZTA,ZrO2 ceramics
Color: White
Density: 3.7-6.05g/cm3
Application: Industrial Machinery
Certification: ISO9001:2015,ROHS
Packaging: Pallet
Productivity: 200000pcs/month
Transportation: Ocean,Land,Air,Express
Place of Origin: CHN
Supply Ability: 200000pcs/month
Certificate: ISO9001:2015,ROHS
HS Code: 8547100000
Port: Shanghai,Shenzhen,Ningbo
Payment Type: T/T,Paypal,Others
Incoterm: FCA,DDP,CIF,FOB,EXW
High Precision Polishing Zirconia Zro2 Ceramic Rod
The excellent mechanical properties, biocompatibility, and resistance to wear and corrosion. Zirconia is a type of ceramic material that is known for its high strength, hardness, and toughness, making it ideal for use in medical applications where durability and reliability are critical.
Zirconia ceramic rods can be used in a variety of medical devices, including dental implants, orthopedic implants, and surgical instruments. Dental implants made from zirconia are gaining popularity due to their superior biocompatibility and the fact that they are less likely to cause allergic reactions than other materials.
Technical Parameters:
Item Unit Al2O3 95%-97% Al2O3 99% Desity g/cm3 3.7 3.85 Flexural Strength Mpa 300 340 Compressive Strength Mpa 3400 3600 Modulus of Elaslicity Gpa 350 380 Impact Resistance Mpa m1/2 4.0 5 Weibull Moudulus m 10.0 10 Vickers Hardness HV0.5 1200.0 1300 Thermal Expansion Coefficent 10-6K-1 5.0-8.3 5.4-8.3 Thermal Conductivity W/mK 24 27 Thermal Shork Resistance △T℃ 250 270 Maximum Use Temperature ℃ 1600 1650 Volume Resistivity at 20℃ Ω ≥1014 ≥1014 Dielectric Constant KV/mm 20 25 Open Porosity % 0 0 Dielectric Constant ξr 10 10 Dielectric Loss Angle Tanσ 0.001 0.001
Item Unit ZrO2 ZTA Desity g/cm3 6.05 4.1 Flexural Strength Mpa 1300 480 Compressive Strength Mpa 3000 3300 Modulus of Elaslicity Gpa 205 320 Impact Resistance Mpa m1/2 12 7 Weibull Moudulus m 25 15 Vickers Hardness HV0.5 1150 1600 Thermal Expansion Coefficent 10-6K-1 10 9 Thermal Conductivity W/mK 2 20 Thermal Shork Resistance △T℃ 280 260 Max Useage Temperature ℃ 1000 1600 Volume Resistivity at 20℃ Ω ≥1010 ≥1012 Open Porosity % 0 0
Except for the ZrO2 Ceramic Parts, we manufacture many other advanced and engineering ceramic parts, like ceramic substrates, ceramic plunger ,Ceramic Disc,ceramic tubes,Ceramic Rod,ceramic tiles ,ceramic grinders, ceramic sealing pistons and so on.