Customized ZTA ceramic plate for pad printing machine China Manufacturer

Customized ZTA ceramic plate for pad printing machine

Payment Type:L/C,T/T,Paypal

Incoterm:FOB,CIF,EXW,Express Delivery

Transportation:Ocean,Land,Air,Express

Port:Shanghai,Shenzhen,Ningbo

$15200-19999Piece/Pieces

$13≥20000Piece/Pieces

Product Attributes
Supply Ability & Additional Information
Packaging & Delivery

Product Attributes

Brand: YXGM

Place Of Origin: China

Species: Ceramic Plates

Application: Industrial Ceramic

Material: Zirconia Ceramic

Processing Service: Cutting, Punching, Moulding

Material: Alumina,ZTA,ZrO2 Cermics

Colour: White

Density: 3.7-6.05g/cm3

Certification: ISO9001:2015.RoHS

Application: coal mining, ore processing, power plants, cement plants, steel plants, chemical plants

Supply Ability & Additional Information

Packaging: Pallets

Productivity: 200000pcs/month

Transportation: Ocean,Land,Air,Express

Place of Origin: CHN

Supply Ability: 200000pcs/month

Certificate: ISO9001:2015,RoHs

HS Code: 6906000000

Port: Shanghai,Shenzhen,Ningbo

Payment Type: L/C,T/T,Paypal

Incoterm: FOB,CIF,EXW,Express Delivery

Packaging & Delivery

Selling Units:

Piece/Pieces

Package Type:

Pallets

Picture Example:

Customized ZTA Ceramic Plate for pad printing machine

Zirconia Toughened Alumina (ZTA) ceramic plate is a specialized product that is used in various industries, including the printing industry. When it comes to a pad printing machine, a customized ZTA ceramic plate can be designed to meet the specific requirements of the machine.

ZTA ceramic plates are known for their superior hardness, excellent wear resistance, and good corrosion resistance. These properties make them ideal for use in pad printing machines, which require durable and long-lasting components.Alumina Ceramic is the material of ZTA ceramic plates and can be used in not only Electrical Ceramics but also Engineering Ceramics.

Technical Parameters:

Item	Unit	Al2O3 95％－97％	Al2O3 99％
Desity	g/cm3	3.7	3.85
Flexural Strength	Mpa	300	340
Compressive Strength	Mpa	3400	3600
Modulus of Elaslicity	Gpa	350	380
Impact Resistance	Mpa m1/2	4.0	5
Weibull Moudulus	m	10.0	10
Vickers Hardness	HV0.5	1200.0	1300
Thermal Expansion Coefficent	10-6K-1	5.0-8.3	5.4-8.3
Thermal Conductivity	W/mK	24	27
Thermal Shork Resistance	△T℃	250	270
Maximum Use Temperature	℃	1600	1650
Volume Resistivity at 20℃	Ω	≥1014	≥1014
Dielectric Constant	KV/mm	20	25
Open Porosity	%	0	0
Dielectric Constant	ξr	10	10
Dielectric Loss Angle	Tanσ	0.001	0.001



Item	Unit	ZrO2	ZTA
Desity	g/cm3	6.05	4.1
Flexural Strength	Mpa	1300	480
Compressive Strength	Mpa	3000	3300
Modulus of Elaslicity	Gpa	205	320
Impact Resistance	Mpa m1/2	12	7
Weibull Moudulus	m	25	15
Vickers Hardness	HV0.5	1150	1600
Thermal Expansion Coefficent	10-6K-1	10	9
Thermal Conductivity	W/mK	2	20
Thermal Shork Resistance	△T℃	280	260
Max Useage Temperature	℃	1000	1600
Volume Resistivity at 20℃	Ω	≥1010	≥1012
Open Porosity	%	0	0