Brand: YXGM
Place Of Origin: China
Species: Ceramic Parts
Application: Industrial Ceramic
Material: Alumina Ceramic
Processing Service: Cutting, Punching, Moulding
Material: 95~99% Al2O3
Color: White,Ivory,Pink
Application: Textile guides
Density: 3.7-3.9g/cm3
Certification: ISO9001:2015,ROHS
Packaging: Pallet
Productivity: 200000pcs/month
Transportation: Ocean,Land,Air,Express
Place of Origin: CHN
Supply Ability: 200000pcs/month
Certificate: ISO9001:2015,ROHS
HS Code: 8547100000
Port: Shanghai,Shenzhen,Ningbo
Payment Type: T/T,Paypal,Others
Incoterm: FOB,CIF,EXW,FCA,Express Delivery
95% ceramic part alumina Textile Ceramic eyelet
A 95% ceramic part alumina textile ceramic eyelet is a small component made from Al2O3 Ceramics material, which has a high alumina content of 95%. It is commonly used in Textile Ceramics machinery, such as spinning and weaving machines, to guide and support the thread or yarn during the production process.
The high alumina content in the ceramic material provides excellent wear resistance, high temperature resistance, and electrical insulation properties. This makes it suitable for use in harsh operating conditions, where the eyelet may be exposed to high temperatures, friction, and electrical currents.
The textile ceramic eyelet is designed with a smooth surface and precise dimensions to ensure smooth thread movement and prevent thread breakage or damage during the textile production process. It is typically installed in the machine's guide or tensioning system, where it acts as a guide for the thread, reducing friction and preventing tangling or snagging.
Overall, the 95% ceramic part alumina textile ceramic eyelet is a durable and reliable component that plays a crucial role in ensuring the smooth and efficient operation of textile machinery.
Technical Parameters:
Item Unit Al2O3 95%-97% Al2O3 99% Desity g/cm3 3.7 3.85 Flexural Strength Mpa 300 340 Compressive Strength Mpa 3400 3600 Modulus of Elaslicity Gpa 350 380 Impact Resistance Mpa m1/2 4.0 5 Weibull Moudulus m 10.0 10 Vickers Hardness HV0.5 1200.0 1300 Thermal Expansion Coefficent 10-6K-1 5.0-8.3 5.4-8.3 Thermal Conductivity W/mK 24 27 Thermal Shork Resistance △T℃ 250 270 Maximum Use Temperature ℃ 1600 1650 Volume Resistivity at 20℃ Ω ≥1014 ≥1014 Dielectric Constant KV/mm 20 25 Open Porosity % 0 0 Dielectric Constant ξr 10 10 Dielectric Loss Angle Tanσ 0.001 0.001