Textile Alumina Ceramic Eyelets,Guides,Rod,Tube China Manufacturer

Textile Alumina Ceramic Eyelets,Guides,Rod,Tube

Payment Type:T/T,Paypal,Others

Incoterm:FOB,CIF,EXW,FCA,Express Delivery

Transportation:Ocean,Land,Air,Express

Port:Shanghai,Shenzhen,Ningbo

$3500-49999Piece/Pieces

$2.5≥50000Piece/Pieces

Product Attributes
Supply Ability & Additional Information
Packaging & Delivery

Product Attributes

Model No.: YXGM-T-08

Brand: YXGM

Material: 95~99% Al2O3

Color: White,Ivory,Pink

Application: Textile guides

Density: 3.7-3.9g/cm3

Certification: ISO9001:2015,ROHS

Supply Ability & Additional Information

Packaging: Pallet

Productivity: 200000pcs/month

Transportation: Ocean,Land,Air,Express

Place of Origin: CHN

Supply Ability: 200000pcs/month

Certificate: ISO9001:2015,ROHS

HS Code: 8547100000

Port: Shanghai,Shenzhen,Ningbo

Payment Type: T/T,Paypal,Others

Incoterm: FOB,CIF,EXW,FCA,Express Delivery

Packaging & Delivery

Selling Units:

Piece/Pieces

Package Type:

Pallet

Picture Example:

99%Al2O3 Ceramic Guides for Textile Machinery

99%Al2O3 Ceramic Guides for Textile Machinery is a kind of ceramic material with high strength, high hardness, high wear resistance and corrosion resistance. It can be used for the production of ceramic guides for textile machinery.

The Alumina Ceramics guide for textile machinery can be used as the guide rail, guide wheel, guide pin, etc., which can be used in the production process of textile machinery. The ceramic guide has the characteristics of high strength, high hardness, high wear resistance and corrosion resistance, which can improve the production efficiency and prolong the service life of the textile machinery.

The ceramic guide for textile machinery is made of 99%Al2O3 ceramic material, which has high strength, high hardness, high wear resistance and corrosion resistance. It is an ideal material for the production of ceramic guides for textile machinery. Our company can provide customized services according to customer requirements.

Technical Parameters:

Item	Unit	Al2O3 95％－97％	Al2O3 99％
Desity	g/cm3	3.7	3.85
Flexural Strength	Mpa	300	340
Compressive Strength	Mpa	3400	3600
Modulus of Elaslicity	Gpa	350	380
Impact Resistance	Mpa m1/2	4.0	5
Weibull Moudulus	m	10.0	10
Vickers Hardness	HV0.5	1200.0	1300
Thermal Expansion Coefficent	10-6K-1	5.0-8.3	5.4-8.3
Thermal Conductivity	W/mK	24	27
Thermal Shork Resistance	△T℃	250	270
Maximum Use Temperature	℃	1600	1650
Volume Resistivity at 20℃	Ω	≥1014	≥1014
Dielectric Constant	KV/mm	20	25
Open Porosity	%	0	0
Dielectric Constant	ξr	10	10
Dielectric Loss Angle	Tanσ	0.001	0.001