Payment Type:T/T,L/C
Incoterm:FOB,FCA,CIF,Express Delivery
Transportation:Ocean,Land,Air,Express,Others
Port:SHANGHAI,NINGBO,SHENZHENG
$3500-49999Piece/Pieces
$2.5≥50000Piece/Pieces
Brand: YXGM
Place Of Origin: China
Types Of: Piezoelectric Ceramics, Dielectric Ceramics, Electrothermal Ceramics, Insulating Ceramics, High Frequency Ceramics
Material: Zirconium Oxide, Alumina-Zirconia, Steatite, Zircon, Zirconia, Alumina, Aluminum Silicate, Boron Nitride, Cordierite, 95%-99%Al2O3
Color: White,Ivory.Pink.Black
Size: Customized
Density: 3.7-3.90g/cm3
Certisfication: ISO9001/2015. Rohs
Packaging: WOODEN CARTON/PALLET
Productivity: 200000 pcs/monthly
Transportation: Ocean,Land,Air,Express,Others
Place of Origin: CHN
Supply Ability: 200000PCS/MONTH
Certificate: ISO9001/2015
HS Code: 8547100000
Port: SHANGHAI,NINGBO,SHENZHENG
Payment Type: T/T,L/C
Incoterm: FOB,FCA,CIF,Express Delivery
Insulating AL2O3 Ceramic coating Holder Base
Insulating AL2O3 ceramic coating holder base refers to a Ceramic Base or substrate made of Al2O3 Ceramics material that has been coated with an insulating layer.
The purpose of this coating is to provide electrical insulation and thermal protection to the base material. AL2O3 ceramic is known for its high thermal conductivity, excellent electrical insulation properties, and resistance to high temperatures.
By adding an insulating coating to the AL2O3 ceramic base, it enhances its Electrical Ceramics insulation capabilities, making it suitable for applications where electrical or thermal insulation is required. This can include electronic components, high-temperature environments, and other industrial applications.
The insulating coating can be made of various materials such as polymers, ceramics, or other insulating materials. It is applied to the AL2O3 ceramic base using techniques like spray coating, dip coating, or electroplating.
The insulating AL2O3 ceramic coating holder base provides a durable and reliable solution for applications that require both the mechanical strength of AL2O3 ceramic and the insulating properties of the coating. It helps to prevent electrical leakage and thermal conductivity between components, ensuring the safe and efficient operation of devices or systems.
Item Unit Al2O3 95%-97% Al2O3 99% Desity g/cm3 3.7 3.85 Flexural Strength Mpa 300 340 Compressive Strength Mpa 3400 3600 Modulus of Elaslicity Gpa 350 380 Impact Resistance Mpa m1/2 4.0 5 Weibull Moudulus m 10.0 10 Vickers Hardness HV0.5 1200.0 1300 Thermal Expansion Coefficent 10-6K-1 5.0-8.3 5.4-8.3 Thermal Conductivity W/mK 24 27 Thermal Shork Resistance △T℃ 250 270 Maximum Use Temperature ℃ 1600 1650 Volume Resistivity at 20℃ Ω ≥1014 ≥1014 Dielectric Constant KV/mm 20 25 Open Porosity % 0 0 Dielectric Constant ξr 10 10 Dielectric Loss Angle Tanσ 0.001 0.001