Payment Type:T/T,L/C
Incoterm:FOB,FCA,CIF,Express Delivery
Transportation:Ocean,Land,Air,Express,Others
Port:SHANGHAI,NINGBO,SHENZHENG
$3500-49999Piece/Pieces
$2.5≥50000Piece/Pieces
Model No.: YXGM-I-010
Brand: YXGM
Place Of Origin: China
Types Of: Piezoelectric Ceramics, Dielectric Ceramics, Electrothermal Ceramics, Insulating Ceramics, High Frequency Ceramics
Material: Zirconium Oxide, Alumina-Zirconia, Steatite, Zircon, Zirconia, Alumina, Aluminum Silicate, Boron Nitride, Cordierite, 95%-99%Al2O3
Color: White,Ivory.Pink.Black
Size: Customized
Density: 3.7-3.90g/cm3
Certisfication: ISO9001/2015. Rohs
Packaging: WOODEN CARTON/PALLET
Productivity: 200000 pcs/monthly
Transportation: Ocean,Land,Air,Express,Others
Place of Origin: CHN
Supply Ability: 200000PCS/MONTH
Certificate: ISO9001/2015
HS Code: 8547100000
Port: SHANGHAI,NINGBO,SHENZHENG
Payment Type: T/T,L/C
Incoterm: FOB,FCA,CIF,Express Delivery
99% Al2O3 Ceramics Insulator Ceramic Insulator part
A ceramic insulator part made of Advanced Ceramics are a high-quality insulator with excellent electrical and thermal insulation properties. It is commonly used in various industries, including electronics, electrical engineering, and high-temperature applications.
The 99% Al2O3 ceramic insulator part is highly resistant to heat, making it suitable for use in high-temperature environments. It can withstand extreme temperatures of up to 1700°C (3092°F) without losing its insulating properties or deforming.
In addition to its high-temperature resistance, this ceramic insulator part also has excellent electrical insulation properties. It has a high dielectric strength, meaning it can withstand high voltages without allowing current to flow through it. This makes it ideal for use in electrical equipment and systems where insulation is critical.
Item Unit Al2O3 95%-97% Al2O3 99% Desity g/cm3 3.7 3.85 Flexural Strength Mpa 300 340 Compressive Strength Mpa 3400 3600 Modulus of Elaslicity Gpa 350 380 Impact Resistance Mpa m1/2 4.0 5 Weibull Moudulus m 10.0 10 Vickers Hardness HV0.5 1200.0 1300 Thermal Expansion Coefficent 10-6K-1 5.0-8.3 5.4-8.3 Thermal Conductivity W/mK 24 27 Thermal Shork Resistance △T℃ 250 270 Maximum Use Temperature ℃ 1600 1650 Volume Resistivity at 20℃ Ω ≥1014 ≥1014 Dielectric Constant KV/mm 20 25 Open Porosity % 0 0 Dielectric Constant ξr 10 10 Dielectric Loss Angle Tanσ 0.001 0.001