Electrical Insulator Alumina Ceramics for Industry Machinery China Manufacturer

Electrical Insulator Alumina Ceramics for Industry Machinery

Payment Type:T/T,Paypal,Others

Incoterm:FCA,DDP,CIF,FOB,EXW

Transportation:Ocean,Land,Air,Express

Port:Shanghai,Shenzhen,Ningbo

$5500-49999Piece/Pieces

$4.5≥50000Piece/Pieces

Product Attributes
Supply Ability & Additional Information
Packaging & Delivery

Product Attributes

Model No.: YXGM-B-001

Brand: YXGM

Place Of Origin: China

Species: Ceramic Parts

Application: Industrial Ceramic

Material: Alumina Ceramic

Processing Service: Cutting, Punching, Moulding

Material: 95-99%Al2O3,ZTA,ZrO2 ceramics

Color: White

Density: 3.7-6.05g/cm3

Application: Industrial Machinery

Certification: ISO9001:2015,ROHS

Supply Ability & Additional Information

Packaging: Pallet

Productivity: 200000pcs/month

Transportation: Ocean,Land,Air,Express

Place of Origin: CHN

Supply Ability: 200000pcs/month

Certificate: ISO9001:2015,ROHS

HS Code: 8547100000

Port: Shanghai,Shenzhen,Ningbo

Payment Type: T/T,Paypal,Others

Incoterm: FCA,DDP,CIF,FOB,EXW

Packaging & Delivery

Selling Units:

Piece/Pieces

Package Type:

Pallet

Picture Example:

Electrical Insulator Alumina Ceramics for Industry Machinery

This Electrical Ceramic Insulator also belongs to Ceramic Base.The material of it is alumina ceramic.Alumina ceramics are a type of electrical ceramic insulator used in a variety of industrial machinery. They are made from a combination of aluminum oxide and other materials, and are extremely durable and resistant to high temperatures. Alumina ceramics are used in a variety of applications, such as in bearings, seals, valves, and other components. They are also used to protect electrical components from damage caused by heat, electrical arcing, and corrosion. Alumina ceramics are highly resistant to wear and tear, making them an ideal choice for industrial machinery.

This Electrical Insulator also belongs to ceramic base.The material of it is alumina ceramics.

Technical Parameters:

Item	Unit	Al2O3 95％－97％	Al2O3 99％
Desity	g/cm3	3.7	3.85
Flexural Strength	Mpa	300	340
Compressive Strength	Mpa	3400	3600
Modulus of Elaslicity	Gpa	350	380
Impact Resistance	Mpa m1/2	4.0	5
Weibull Moudulus	m	10.0	10
Vickers Hardness	HV0.5	1200.0	1300
Thermal Expansion Coefficent	10-6K-1	5.0-8.3	5.4-8.3
Thermal Conductivity	W/mK	24	27
Thermal Shork Resistance	△T℃	250	270
Maximum Use Temperature	℃	1600	1650
Volume Resistivity at 20℃	Ω	≥1014	≥1014
Dielectric Constant	KV/mm	20	25
Open Porosity	%	0	0
Dielectric Constant	ξr	10	10
Dielectric Loss Angle	Tanσ	0.001	0.001

Item	Unit	ZrO2	ZTA
Desity	g/cm3	6.05	4.1
Flexural Strength	Mpa	1300	480
Compressive Strength	Mpa	3000	3300
Modulus of Elaslicity	Gpa	205	320
Impact Resistance	Mpa m1/2	12	7
Weibull Moudulus	m	25	15
Vickers Hardness	HV0.5	1150	1600
Thermal Expansion Coefficent	10-6K-1	10	9
Thermal Conductivity	W/mK	2	20
Thermal Shork Resistance	△T℃	280	260
Max Useage Temperature	℃	1000	1600
Volume Resistivity at 20℃	Ω	≥1010	≥1012
Open Porosity	%	0	0