Types Of: Piezoelectric Ceramics, Dielectric Ceramics, Electrothermal Ceramics, Insulating Ceramics, High Frequency Ceramics
Material: Zirconium Oxide, Alumina-Zirconia, Steatite, Zircon, Zirconia, Alumina, Aluminum Silicate, Boron Nitride, Cordierite, 95%-99%Al2O3
Color: White,Ivory.Pink.Black
Size: Customized
Density: 3.7-3.90g/cm3
Certisfication: ISO9001/2015. Rohs
Packaging: WOODEN CARTON/PALLET
Productivity: 200000 pcs/monthly
Transportation: Ocean,Land,Air,Express,Others
Place of Origin: CHN
Supply Ability: 200000PCS/MONTH
Certificate: ISO9001/2015
HS Code: 8547100000
Port: SHANGHAI,NINGBO,SHENZHENG
Payment Type: T/T,L/C
Incoterm: FOB,FCA,CIF,Express Delivery
96%Al2O3 Ceramics insulation base for Air heater
Al2O3 ceramics with a 96% purity is commonly used as an insulation base for air heaters due to its excellent thermal and Electrical Ceramics insulation properties.
Al2O3 ceramics have a high melting point (approximately 2040°C) and low thermal conductivity, making them ideal for applications where high temperatures need to be maintained without significant heat loss. This ensures efficient heating of the air passing through the heater.
Additionally, Al2O3 ceramics have excellent electrical insulation properties, making them suitable for use in electrical heating elements. They can withstand high voltages without conducting electricity, minimizing the risk of electrical accidents.
Furthermore, Al2O3 ceramics are chemically inert and resistant to corrosion, ensuring a long lifespan for the insulation base. They can withstand harsh environments and exposure to various chemicals without degradation.
Overall, the 96% Al2O3 ceramics insulation Ceramic Base for air heaters provides reliable thermal and electrical insulation, high temperature resistance, and chemical resistance, making it an ideal choice for this application.
Technical Parameters:
Item Unit Al2O3 95%-97% Al2O3 99% Desity g/cm3 3.7 3.85 Flexural Strength Mpa 300 340 Compressive Strength Mpa 3400 3600 Modulus of Elaslicity Gpa 350 380 Impact Resistance Mpa m1/2 4.0 5 Weibull Moudulus m 10.0 10 Vickers Hardness HV0.5 1200.0 1300 Thermal Expansion Coefficent 10-6K-1 5.0-8.3 5.4-8.3 Thermal Conductivity W/mK 24 27 Thermal Shork Resistance △T℃ 250 270 Maximum Use Temperature ℃ 1600 1650 Volume Resistivity at 20℃ Ω ≥1014 ≥1014 Dielectric Constant KV/mm 20 25 Open Porosity % 0 0 Dielectric Constant ξr 10 10 Dielectric Loss Angle Tanσ 0.001 0.001